Diffuser of active agents such as insecticides, perfumes, detergents or disinfectants, and manufacturing process thereof

ABSTRACT

Diffuser of an active liquid agent, for the treatment of a fluid environment, be it at the gaseous or liquid state, of the type including a container (1) of the active agent, closed by grid element apt to maintain in position the active agent and to allow the emanation of fluids of the same, the grid element being covered by a barrier film, peelable at the time of the first use to make operative the grid element, wherein the container (1) is closed by a single multilayer film (2, 3a, 3b) including at least one external barrier layer (3a) and at least another inner sealing layer (2) apt to maintain in position the active agent and to form the grid element, at the time of the first use of the container, following the simultaneous removal of the barrier film and of predefined portions of the sealing layer.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. patent application Ser. No. 16/066,880 filed on Jun. 28, 2018, which is the national phase of PCT International Application No. PCT/IB2016/058034 filed on Dec. 28, 2016, which claims priority to IT Patent Application No. 102015000089512 filed on Dec. 31, 2015, the contents of which are hereby incorporated by reference.

FIELD OF THE INVENTION

The present invention relates to a diffuser of active liquid agents—such as for example insecticides, perfumes, detergents or disinfectants—for the treatment of a surrounding fluid environment, be it at the gaseous or liquid state, that are imbued in a solid or gel-like support. Such a diffuser is of the type having at least one wall closed by a containment grid of the solid or gel-like support of the active agent and by a removable external barrier film, impermeable to fluids, which covers the active agent and the grid during the diffuser storage and transport steps. The invention also relates to a manufacturing process of such a diffuser.

PRIOR STATE OF THE ART

Devices consisting of a box-shaped container of the above indicated type are well known in the art; they are used to make up a large supply of active agents which—as it happens for many products treating a liquid or gaseous environment—are sufficiently soluble or evaporable in the fluid of which said environment consist, to cause a slow release of the active agent towards the environment, through said grid. Said emission may possibly be accelerated with the aid of an additional heating of the fluid flowing around the device.

In known diffusers, the grid has the following functions:

-   -   retaining the active agent support in a correct and stable         position inside the diffuser;     -   avoiding the contact between the active agent and the hands or         other parts of the user's body;     -   allowing the emission of the active agent towards the         surrounding environment, once the external barrier film has been         removed;         and is made of a solid material, preferably an injection-moulded         plastic material.

As already said, in order to prevent the diffusion of the active agent from starting before the first use of the diffuser by the user, an external barrier film impermeable to fluids is applied onto the external side of the grid. A stable adhesion between the grid material and the external barrier film is obtained by means of an adhesive or by thermal welding. The adhesion strength between these two elements must be sufficiently high to prevent the active agent from leaking between the grid and the external barrier film or the external barrier film from accidentally detaching during transport, storage and sale, and yet still sufficiently low to allow the user to remove the external barrier film at the time of use without excessive effort.

Normally, the remaining surface of the diffuser body consists of continuous walls of plastic material, which the active agent cannot pass through; it is possible to provide a second grid also on the opposite side of the diffuser body, in order to have a higher overall emission rate of the active agent.

The following are mentioned among the drawbacks of the existing solutions of this type:

-   -   as said above, the grids are usually made of injection-moulded         plastic material; this involves the production of a separate         element in addition to the container, which has its own cost of         production and an additional cost for assembling it on of the         diffuser body, before the application of the external barrier         film;     -   the application process of the external barrier film on the grid         has a certain complexity (label positioning, non-flatness of the         injection-moulded piece, positioning differences between pieces,         etc.) possibly resulting in an impairment of the final quality         of the manufactured item;     -   the active substance may interact with the adhesive layer during         its application or hinder the thermal welding process thus         leading to an early separation of the external barrier film from         the grid.

SUMMARY OF THE INVENTION

The object of the invention is therefore to provide a structure for a diffuser that:

-   -   overcomes the above mentioned drawbacks in the manufacturing         process of the known-type diffusers, by reducing the number of         pieces to be manufactured and consequently simplifying the         assembly step;     -   provides better performances with reference to the adhesion         stability of the external barrier film and, consequently, to any         possible active agent leaking;     -   allows the user an easier start-up operation of the activation         function of the diffuser; and, finally,     -   exhibits a reduced manufacturing cost compared to diffusers of         the known art.

This multiple object is fully achieved by a diffuser of an active liquid agent, for the treatment of a fluid environment, be it at the gaseous or liquid state, of the type comprising a container (1) of the active agent, closed by grid means apt to retaining in position said active agent and to allow the emanation of fluids of the same, said grid means being covered by a barrier film, peelable at the time of the first use to make operative said grid means, wherein said container (1) is closed by a single multilayer film (2, 3 a, 3 b) comprising at least one external barrier layer (3 a) and at least another inner sealing layer (2) apt to retaining in position said active agent and to form said grid means, at the time of the first use of the container, following the removal of said barrier film and of predefined portions (4) of said sealing layer (2).

Other preferred features of the invention are disclosed in the dependent claims.

BRIEF DESCRIPTION OF THE DRAWINGS

Further features and advantages of the invention will anyhow be more evident from the following detailed description of some preferred embodiments of the same, provided as a mere and non-limiting example and illustrated in the attached drawings, wherein:

FIG. 1 is a perspective view of a diffuser according to a first embodiment of the invention, in the closed configuration prior to use;

FIG. 2 is a view similar to FIG. 1, taken while removing, by peeling it, part of the multilayer film which closes the diffuser;

FIG. 3 is a perspective view similar to FIG. 2, with part of said multilayer film completely removed;

FIGS. 4a and 4b are schematic, greatly enlarged, cross-sectional views, of the whole multilayer film (FIG. 1) and of the portion of said multilayer film that remains adhering to the container after the opening of the diffuser device (FIG. 3), respectively;

FIG. 5 is an exploded perspective view of a second embodiment of the diffuser of the present invention;

FIG. 6 is a view similar to FIG. 5, after the sealing film partial removal;

FIG. 7 is an exploded perspective view of a third embodiment of the diffuser of the present invention; and

FIG. 8 is a view similar to FIG. 7, after the sealing film partial removal.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

As outlined in FIGS. 1 to 3, a diffuser according to the present invention consists of a container body 1 for the active liquid agent, and a multilayer film 3, which is welded to the body 1. The active liquid agent can be totally imbued in a solid or gel-like support, or it can be contained in a reservoir which is separated from the multilayer film by a solid support apt to be imbued with the active liquid agent and which therefore acts as a wick. In any case, thus, the multilayer film 3 is in contact with a solid internally, and in contact with the environmental fluid, in the gaseous or liquid state, externally.

According to the present invention, the multilayer film 3 is directly applied on the edge of the container 1 and is able to serve both as a grid and an external barrier layer, which functions, in known diffusers, were performed by two separate components. In order to achieve this innovative and striking result, the closing multilayer film consists of the following coupled layers:

-   -   an inner sealing layer 2, apt to maintain in stable position the         solid or gel-like support of the active agent, which has an         inner structure of incisions which run through the entire         thickness of said layer, according to a predefined pattern;     -   an external barrier layer 3 a, apt to prevent the active agent         from leaking outwards;     -   an intermediate release layer 3 b, apt to facilitate the         detachment by peeling between said intermediate release layer 3         b and the inner layer 2, when a sufficient traction effort is         imparted to the external barrier layer 3 a through its         projecting tab 3′.

Optionally, a further layer (not shown in the figures) can be applied on the external barrier layer 3 a, the whole to confer to the same additional chemical and/or mechanical protection.

The inner layer 2 of the multilayer film of the present invention can be defined as a layer “provided with an inner structure of incisions” or more briefly as a “structured” layer, because this layer is cut throughout its depth according to one or more closed lines of a desired shape, which delimit the perimeter of incision areas 4 which are therefore no longer laterally connected to the remaining part of the film 2. Thus, when the peelable part of the multilayer film 3—i.e. both the layers 3 a and 3 b—are removed, through the tearing action on tab 3′, the incision areas 4 of the inner sealing layer 2 remain adhering to the overlying intermediate release layer 3 b and they are removed with it, while on the free surface of the container 1 remains only the part 5 of the inner sealing layer 2, freed from the incision areas 4, therefore having a plurality of orifices 6. In this way, this part 5 of the inner sealing layer 2 is therefore able to perform the same functions as seen above for the grid of the known-art diffusers, i.e. keeping the solid or gel-like active agent support in position, while allowing the emission of the agent to the surrounding fluid environment, be it at a gaseous or liquid state, in the form of vapours or solution, respectively.

In order to obtain that the incision areas 4 of the inner sealing layer 2 remain adhering to the layer 3 b while the portion 5 of inner sealing layer 2 remains adhering to the edge of the container, it is sufficient to operate as follows: on one hand, care is taken to secure the contour of the multilayer film, and therefore of its inner sealing layer 2, to the upper flange edge of the container 1 in a particularly accurate manner, for example by thermal welding, so that this fixing offers a great mechanical strength in terms of detachment from the container 1. On the other hand, a structure of incision areas is formed in the inner sealing layer 2 with the following conformation: the incision areas are delimited by a closed perimeter; the incisions go through the entire thickness of the inner sealing layer 2; the incision areas preferably do not intersect; and, preferably, the incision areas do not extend in the perimeter area of the inner sealing layer 2, so that the remaining part 5 of this inner sealing layer, after removal of said incision areas 4, still has a sufficient mechanical strength.

In this way, when the external barrier layer 3 a and the intermediate release layer 3 b of the multilayer film are removed by peeling, by pulling the tab 3′, the perimeter edge of the inner sealing layer 2—which, as said, is firmly fixed to the flange edge of the container 1—together with the remaining portion 5 of the same inner sealing layer, remains adhering to the container 1; while the incision areas 4—which, as a result of said incisions, are no longer joined laterally to the remaining part of the sealing layer 2—will be removed thanks to their adhesion to the intermediate release layer 3 b.

The depth of said closed-perimeter incision lines is not necessarily strictly limited to the inner sealing layer 2, but it can extend further within the intermediate release layer 3 b and possibly also affect the entire thickness of this intermediate release layer 3 b, thus making the adjustment of the cutting depth during the manufacturing process less critical. Obviously, it is preferable that the cutting action not to reach the external barrier layer 3 a, typically of aluminium, so as not to risk damaging the integrity of this external barrier layer, which action could reduce the overall barrier properties of the multilayer film of the present invention.

A cutting process for manufacturing such a multilayer film according to the invention is the one which provides for the use of a standard Form Fill Seal machine type, commonly used in the flexible packaging industry, and to perform the cutting operation of the inner sealing layer 2 in a stage preceding the sealing closure of the container 1. In this way, it is possible to obtain more easily a good positioning of the different incision areas 4 with respect to the inside of the cavity of the container 1.

The incision can be done mechanically, with blades designed to reach a certain depth inside the inner sealing layer 2, and optionally the intermediate release layer 3 b. Alternatively, the cut can be made using a thermal-action knife (thermocutter) which can dissolve the plastic material layer 2. Preferably, the cut will be rather performed using laser cutting technology, where the applied power control can be performed in a very precise way, so as to achieve a certain desired cutting depth. This latter process is particularly preferred because it does not involve specific mechanical equipment according to the cutting pattern, so that different patterns of incision areas 4 may be obtained with the same cutting machine, thus allowing to manufacture products with different features and performances just by appropriately programming said cutting machine. It is quite clear that the distribution and the geometry of the incision areas 4 will be defined from time to time according to the specific application requirements.

In the following, the diffuser of active agents of the present invention will be described with reference to some specific examples of application.

Example 1—Container of Active Agents on a Solid Support (FIGS. 1-3)

The container 1 is made from a PE plastic material, 1.5 mm thick, injection moulded in the shape of a circular cup with a diameter of 50 mm.

Inside this container 1 a cellulose pad is placed, impregnated with an active liquid substance (perfume, disinfectant, insecticide, etc.) having similar dimensions to the inner diameter of the circular cup, so as to find a stable position within the container.

A multilayer film according to the invention is positioned on top of the container and heat-sealed on the contour flange of the cup of the container 1.

The multilayer film consists of, from inside outwards, a PE inner sealing layer 2, a PP intermediate release layer 3 b, an aluminium external barrier layer 3 a, and by a further external PET protection layer.

The PE inner sealing layer 2 is cut according to multiple incision areas 4, having a circular geometrical shape with a diameter of about 2 mm. Their position is distributed in a regular manner in correspondence with the central area of the container 1.

When the aluminium external barrier layer 3 a is removed, together with the PP intermediate release layer 3 b, the PE material corresponding to the above multiple incision areas 4, formed in the inner sealing layer 2, is simultaneously removed, creating round holes 6 in said PE inner sealing layer 2. Through these holes 6, the active substance imbued in the pad—in the form of vapour or solution, depending on whether the container 1 is positioned in a gaseous or liquid environment—can be emanated, while the pad itself is kept in position and inhibited from contact with the user from the remaining portion 5 of the PE inner sealing layer 2.

Example 2—Container of Active Liquid Agents with Wick (FIGS. 5-6)

The container 1 in this case consists of a sheet of PET/EVOH/PE, having a thickness of 450 microns, thermoformed so as to have a flat perimeter flange and a central cavity that comprises two different depth zones; more precisely, an area with greater depth of about 20 mm, for containing the active liquid agent 8, and an area elongating upward having a much lower depth of about 2 mm.

A porous cellulose element 7 having a Y-shape and thickness of about 2 mm, which acts as a wick, is disposed between the container 1 and the multilayer film 3, inhibiting a direct contact between said multilayer film 3 and the active liquid agent 8. The elongated portion of the wick 7 is disposed in the cavity of lesser depth of the thermoformed container 1, while the two diverging ends of the Y shape are placed in respective low-thickness cavities formed in the perimeter flange.

The multilayer film consists, as in the previous Example, of a PE inner sealing layer 2, a PP intermediate release layer 3 b, an aluminium external barrier layer 3 a and a further PET external protection layer.

The PE inner sealing layer 2 is cut according to a circular incision area, so as to create in the same—after peeling of the external barrier layer 3 a and of the intermediate release layer 3 b, by acting on tab 3′—a single circular orifice 6 of the diameter of 10 mm in an area facing the central part of the wick. Preferably, in the process of application of the multilayer film to the container 1, the edge of such circular orifice 6 is welded to the wick 7, so as to avoid any possible leaking of active liquid agent between the wick and the multilayer film.

The container thus formed can then be directly associated with a heating device to obtain the emanation of the active agent at a controlled temperature above room temperature.

Example 3—Container of Active Liquid Agents with Wick (FIGS. 7-8)

A container 1 is formed in the same manner described in Example 2 and a similar wick 7 is disposed in the same. The multilayer film consists, as in the previous Example, of a PE inner sealing layer 2, a PP intermediate release layer 3 b, an aluminium external barrier layer 3 a and a further PET protection layer, in which a circular orifice 6 is cut as in Example 2.

Unlike the previous example, the PE inner sealing layer of the multilayer film is, however, permeable only to vapours of the active agent. In addition, a guide 9 and an incision line 10 are formed on the external barrier layer 3 a in the manner described in detail in the Italian patent application no. 102015000022867, in the name of the same Applicant.

In this combined solution, when the user activates the device by means of peeling the external barrier layer 3 a, the external barrier layer is removed only in its upper portion while it remains intact in the lower part which covers the portion of the active agent reservoir 8 having a greater depth.

Thanks to this construction, it is therefore possible to use the diffuser of the invention either in the same way described in the above-mentioned patent, i.e., by exploiting only the natural evaporation rate of the active substance, or by combining the diffuser with a heating device, to obtain an increased active agent emanation, through the wick 7 and the orifice 6.

It is understood, however, that the invention is not to be considered as limited by the particular arrangements illustrated above, which represent only exemplary implementations of the same, but different variants are possible, all within the reach of a person skilled in the art, without departing from the scope of the invention itself, as defined by the following claims. 

1. A diffuser of an active liquid agent imbued in a solid or gel-like support, for the treatment of a gaseous or liquid environment, the diffuser comprising: a container of the active liquid agent, closed by a grid configured to maintain in position the solid or gel-like support of said active liquid agent and to allow emanation of fluids of the active liquid agent, said grid being covered by an external barrier film that is configured to be peeled off of the diffuser at a first use of the container in order to make the grid operative to allow emission of the active liquid agent, wherein the container is closed by a single multilayer film comprising at least the external barrier layer, an inner sealing layer, and an intermediate release layer between the external barrier layer and the inner sealing layer, the inner sealing layer being internally structured with predefined incision portions which run through an entire thickness of the inner sealing layer according to a predefined pattern such that the predefined incision portions of the inner sealing layer are not laterally connected to a remaining part of the inner sealing layer and adhere to the external barrier layer, wherein the inner sealing layer is configured to form the grid, at the first use of the container, when the external barrier layer and the predefined incision portions of the inner sealing layer are simultaneously removed from the container.
 2. The diffuser as in claim 1, wherein said external barrier layer is configured to prevent outward leaking of the active agent, and said intermediate release layer is configured to facilitate detachment by peeling between said intermediate release layer and the inner sealing layer, when a sufficient traction effort is imparted to the external barrier layer.
 3. The diffuser as in claim 2, wherein said inner sealing layer is a PE plastic material, said intermediate release layer is a PP plastic material, and said external barrier layer is aluminum.
 4. The diffuser as in claim 1, wherein a peripheral inner edge of the inner sealing layer of said multilayer film is thermally welded onto a flange edge of said container.
 5. The diffuser as in claim 1, wherein said inner sealing layer is internally structured with the predefined incision portions, according to one or more closed lines which delimit a perimeter of said predefined incision portions.
 6. The diffuser as in claim 5, wherein said predefined incision portions of the inner sealing layer remaining adherent to said external barrier layer, leave corresponding cavities in said inner sealing layer, upon the removal of said external barrier layer.
 7. The diffuser as in claim 1, wherein said active liquid agent is separated from said multilayer film by a porous solid support acting as a wick.
 8. The diffuser as in claim 7, wherein said inner sealing layer is permeable to the vapors of said active liquid agent.
 9. The diffuser as in claim 7, wherein said inner sealing layer is welded to said porous solid support acting as the wick, in correspondence to edges of orifices formed in the inner sealing layer.
 10. A manufacturing process for the diffuser as in claim 1, the process comprising: forming said single multilayer film, with at least the inner sealing layer and at least the external barrier layer; cutting at least said inner sealing layer according to closed-perimeter incision lines which run through an entire thickness of said inner sealing layer, according to the predefined pattern which defines the predefined incision portions that are no longer laterally connected with the remaining part of said inner sealing layer; and applying and accurately welding an inner edge of said multilayer film onto a flange edge of said container.
 11. The process as in claim 10, further comprising disposing the intermediate release layer between the inner sealing layer and the external barrier layer.
 12. The process as in claim 10, wherein said incision lines extend at least partly into said intermediate release layer.
 13. The process as in claim 10, wherein said incision lines are performed mechanically, with cutting blades at a controlled cutting depth.
 14. The process as in claim 10, wherein said incision lines are performed thermo-mechanically, with thermal-action knives with controlled cutting depth.
 15. The process as in claim 10, wherein said incision lines are performed with a laser cut, adjusting the cutting depth by controlling the applied power. 